Filled PTFE - Filler Functions

Glass Filled PTFE
PTFE is reinforced with glass fibres, the percentage varying between 5 and 40%. The added glass fibre improves the wear properties and, to a minor degree, also the deformation strength under load while leaving substantially unchanged the electrical and chemical characteristics. Glass itself, has a rather poor resistance against alkalis and is easily attacked by hydrofluoric acid. The coefficient of friction is slightly increased and for this reason, graphite is sometimes added to compensate this side effect.  Buy Glass Filled PTFE online

Carbon Filled PTFE
Carbon is added to the PTFE in a percentage by weight between 10 and 35%, along with small percentage of graphite. Also, the carbon tends to improve to a considerable degree, wear and deformation strength, while leaving practically unchanged the chemical resistance, but substantially modifying the electrical properties.  Buy Carbon Filled PTFE online

Bronze Filled PTFE
Bronze, when used as filler, is added in percentages of weight between 40 and 60%. Bronze filled PTFE has the best wear properties, remarkable deformation strengths and good thermal conductivity, but poor electrical characteristics and chemical resistance.

Graphite Filled PTFE
The percentages used vary between 5 and 15%. Graphite lowers the coefficient of friction and is, therefore, often added to other types of filled PTFE for improving this property. It improves the deformation under load, strength and, to a minor degree, the wear properties.

Other Available Fillers
Molybdenum sulphide, though decreasing the coefficient of friction, is sometimes preferred to graphite. Some metal powders (stainless steel, nickel, titanium), in consideration of their particular resistance to chemical agents, are sometimes used as fillers for PTFE, even though their wear resistance, with respect to bronze, are inferior. The metal oxides, added to other fillers, give better wear properties.

Physical & Mechanical Properties of Filled PTFE  [Back to Top]

Wear
The contact between two sliding surfaces, because of the inevitable friction generated in the contact zone, results in a certain wear whose magnitude depends on load, speed and time of sliding contact. Theoretically, between these parameters and the resulting wear exists a relation proportional to:

R = KPVT

where, expressed in the measuring units of table:
R = wear in mm
P = specific load in N/mm2 (referring to the surface - Ø x l - in case of bushes, nipples, etc.)
V = sliding speed in m/sec
T = time in hrs
K = wear factor in mm3 sec/Nmh.

The value of the factor PV after which the coefficient of wear loses its linear behavior, assuming remarkable values with the system passing from weak to strong wear condition, is known as "PV limit". This PV limit and the wear factor are, therefore, characteristic parameters of each material. In practice, however, it can be easily perceived, the wear factor and the PV limit of the same filled material can vary also with the nature, the hardness and the surface finish of the other contact "partner" with the presence, or not, of cooling and/or lubricating fluids.

Deformation under load and compressive strength
PTFE, like most other plastic materials, has no "elastic zone" where the ratio load/deformation (Young modulus) has a constant value. This ratio load/deformation depends upon the time of application of the load and the ensuing deformations; this phenomenon is known as "creep", and at the removal of the load, there is only a partial return of the deformation to the original state ("elastic recovery"), so that we are always in the presence of a "permanent deformation".

Creep, obviously not being a linear function of time, results after just over 24 hrs in deformations which in most cases are not taken into consideration. With increasing temperature, there is a falling off of the deformation under load properties and consequently of the compressive strength which is already at 100°C equal to 1/2 of that at 23°C and at 200°C about 1/10th.

In any case, PTFE and in particular filled PTFE, is one of the plastic materials retaining, at high temperatures, optimum deformation properties under load. To conclude, the elastic recovery in about 50% of the deformations under load, and the permanent deformations are equal to about 50% of the deformations under load.

This applies both to filled and unfilled PTFE. The properties of the first are however decidedly superior. In fact, the deformation under load of the more common types of filled PTFE are about 1/4 of that of the unfilled ones, while the compressive strength is about the double.

Thermal Properties of Filled PTFE  [Back to Top]

The thermal expansion of filled PTFE is in general inferior to that of unfilled PTFE and always greater in the direction of the moulding than crosswise. The thermal conductivity is superior to that of unfilled PTFE, particularly when using fillers having a high thermal conductivity of their own.

Filled PTFE therefore have better thermal properties than the unfilled ones.

Electrical Properties of Filled PTFE  [Back to Top]

These properties depend to a large degree upon the nature of the filler. Only PTFE filled with glass fibre possess good dielectric properties, even though different from those of unfilled PTFE. For example, the volume and surface resistivity, the dielectric constant and the dissipation factor vary largely with the variation of the humidity and frequency.

Back to Top